Rubber Abrasion Test

Wear of rubber products is a common phenomenon of destruction, it is a friction caused by the phenomenon of micro-off the rubber surface, The good or bad wear and tear properties of rubber products to a large extent determine the product life.Tires, conveyor belts, rubber shoes, hoses and many other products use life directly related wear resistance, and thus wear resistance is an important technical indicators of rubber performance.

In order to test the performance of rubber wear, there has designed the Akron, Lambert abrasion testing machine, Schopper abrasion test machine, Pico abrasion and other models of abrasion testing machine, generally under the stipulate conditions of test with the friction contact surface, Use the weight or volume of rubber particles express test result , In China's current rubber products technical standards, wear resistance is mostly based on Akron abrasion test machine .

1. Rubber Akron abrasion test

Test principle: the sample and the grinding wheel at a certain tilt angle and a certain load under the action of friction, test the sample stroke 1.6lkm mileage wear volume.

Rubber Akron abrasion test machine model:RT-107

2 Rubber roller DIN abrasion test

In many rubber products test, abrasion test is an indispensable test. For many rubber products, wear performance is directly related to its service life, has big practical significance, it is one of the important technical indicators. So abrasion performance testing is a very important issue in rubber industry . Over the years in China testing the performance of rubber wear test equipment used the Akron abrasion test machine and the Grazi abrasion testing machine, the two abrasion test machine are able to test the rubber abrasion performance, but the test cycle is too long and test path repetition and other deficiencies. Rotary roller abrasion machine compared with the commonly used Akron abrasion test machine and Glaxi abrasion test machine , it has the advantage of small sample, short test cycle and no repeat friction path, etc., it is the more popular international common abrasion test machine.

Test principle: under the specified contact pressure and area, the test sample be friction in a certain level of sand generated the amount of abrasion. The abrasive cloth is attached to the surface of the rotary roll, and the sample is pressed against a roller with an abrasive cloth to move the specimen laterally along the roll. Wear is produced at one end of the cylindrical specimen, measuring the mass loss of the sample, and calculating the volume of wear from the density of the sample. The test results are expressed in terms of volume wear or wear index relative to a standard index.

Rubber roller abrasion test machine model:RT-106

Dongguan Right Testing Machine Co.,Ltd

What’s the heating system of Plate Vulcanizing Press Machine?

Flat vulcanizing press machine has two types heating ,electronic heating and steam heating, mainly by the host, hydraulic system, electronic control system composed of three major parts,

Fuel tank installed alone on the host left, not the impact of hot plate temperature; operating valve installed on the host left ,the worker is convenience to operate  and visual spacious.

1.Electronic heating

Flat Plate Vulcanizing Press Machine system uses three-phase four-wire power supply, the machine housing should be reliable grounding to ensure safety, the line is generally should not be less than 4~6m ㎡, and peripheral circuit breaker for protection. When the power is turned on, turn the combination switch Q to the ON position, And then start the SB2 button, pump motor work, flat plate up, with pressure increasing, when the pressure up to the setting pressure,pressure table connation point connected, the pump motor to stop working, the machine enter the curing state, time relay KT1 started in seconds unit with timing. If the process of work pressure down (means black needles leave the red needle) and reach the green needle position, the system will be connected to oil pump motor for supply pressure, until reach to predetermined pressure. Manual pressure can also be carried out (ie, press the SB2 button) to reach supply the pressure when pressure down.

Any half-way automatic pressure-filling operation does not affect the curing time, after finished curing buzzer alarm to prompt the worker can open mold. Alarm time set by the KT2, before ex-factory set about 10 seconds, the user can adjust, or press SB1 to interrupt the alarm. In case of abnormal phenomenon, should check the electrical box relay is intact, loose or out drop. In the event of an emergency, press the SB1 stop button, the machine oil pump to stop working.

2.Steam heating

If Plate Vulcanizing Press Machine use steam heating for curing process, the hot plate heating is through the industrial steam pipe to transport the steam from the machine inlet, and then through the steam pipe to the distribution of the hot plate, each hot plate with a soft metal pipe connection, the vapor pressure can be read from the barometer (maximum steam pressure <1MPa). Condensate water in the hot plate and part of flue gas through the pipe outlet derivation, Needed steam (Or cooling water), as well as condensed water, waste gas and so on by the pipeline valve to control.